@article{oai:air.repo.nii.ac.jp:00001338,
 author = {大塚, 健治 and 田上, 道弘 and 佐藤, 伸 and 武藤, 侃 and OTSUKA, Kenji and TAGAMI, Michihiro and SATOU, Shin and MUTOU, Akira},
 issue = {1},
 journal = {素材物性学雑誌},
 month = {Aug},
 note = {Effects of Ti content on the reaction products of AL03- Kovar joints were
studied using active filler metal. The variation of microstructures of reaction
products formed at the interface between ALO, and active filler metal was investigated
by scanning electron microscopy, auger electron microscopy and xray
diffraction.
Increace of Ti content in the active filler metal improves shear strength of
Al,03- Kovar joints brazed at 1123K for 900s and addition of 8.1mass% Ti improves
shear strength about 40% at the same brazing condition. Reaction layer
(TiO) containing higher Ti content were formed in the interface between active
filler metal and Al20, and these reaction layers are attributed to higher shear
strength of Al203- Kovar joints.},
 title = {アルミナとコバール接合体の反応層に及ぼすろう材中のTi量の影響},
 volume = {11},
 year = {1998}
}